An alkaline condition allowed the creation of a calcium acetylacetonate/zinc mixture using zinc-nitrate hexahydrate and calcium chloride. It’s used as an additional heat stabilizer for polyvinylchloride. PVC products were tested for thermal stability using Congo red test and oven heat. These results revealed that PVC products had a synergistic effect when they were heated to 70 degrees Celsius. PVC testing pieces became completely blackened after 110 minutes. Acetone calcium. Also, the addition of a mass fraction of 1.2% calcium acetylacetonate/zinc, thermal stability time of up to 81min, PVC test piece to 190 min wholly blackened and better than the commonly used epoxy soybean oil and dipentaerythritol auxiliary class Heat stabilizers.
A polyvinylchloride PVC is a versatile material that has great properties, including low cost and corrosion resistance. Also, it’s strong, flame-resistant, and strength. It can be used to make building materials, chemicals, packaging, among other areas, making it one of the five best-selling general-purpose plastics in the world. PVC has poor thermal properties. PVC products are best processed at around 180°C. Once the temperature gets to 130°C, PVC begins to lose its thermal stability and releases toxic hydrogen chloride gas. PVC products become darker and have lower mechanical and mechanical property. PVC is. Addition of heat stabilisers to products is a crucial measure. Heat stabilizers that are currently being used include metal soaps, organotins and metal salts. Heat stabilizers containing lead are dangerous for humans and the environment. Therefore, they are gradually being replaced. The disadvantages to organotins which have excellent performance include their high cost and low thermal stability. An auxiliary heat stabiliser is required in order to increase the heat stability.
The toxicity level of the heat stabilizer b-diketone is extremely low. It’s widely used in auxiliary stability for metal soaps. Current –diketones calcium and zinc are typically synthesized separate, so their coloration in PVC products may be tested independently.
PVC auxiliary Heat Stabilizer acetylacetonate/zinc Composite was synthesized at room temperatures based upon the synergistic impact of calcium acetylacetonate/zinc on PVC’s thermal stability. A variety of characterisation methods were used to identify the product. The metal soap melt stabilizer calciumstearate was also added to PVC to test the effect of the additive on PVC’s thermal stability.
Calcium acetylacetonate/zinc falls under the –diketone sodium-assisted Heat Stabilizer. It has the exact same heat stabilizing mechanism as –diketone. The PVC product is capable of removing HCl while heating. Furthermore, if there are a lot more conjugated double links, it will darken the PVC product. In contrast, the heat stabilizer mechanism of the calcium acetylacetonate/zinc alloy can absorb HCl gas from PVC and give rise to acetylacetone. ZnCl2 catalysis will produce acetylacetone.
In oven heat aging tests and Congo-red testing, it was found that the combined effect of zinc molar/calcium acetylacetonate was optimal. The single component acetylacetonate had a shorter heat stability time. Copper calcium or zinc acetylacetonate. With a PVC Mass fraction of 1.2% Calcium Acetylacetonate/Zinc Acylacetonate having a molar ratio 15:1, thermal stability is achieved at 81 min. This is much better than common auxiliary heat stabilisers epoxy soybean oil, double and triple. Pentaerythritol.
A calcium acetylacetonate/zinc alloy material greatly increases the thermal stability. This is because it absorbs HCl. Acetylacetone ligand then replaces the active allylchloride on PVC by acetylacetone ligand. Acetyl Acetone also absorbs excess ZnCl2 which reduces its concentration.
Cataniadagiocare advancedmaterial Tech Co., Ltd., (Cataniadagiocare), has over 12 year experience in chemical product development. You can contact us to request high quality Calcium Dodecyl Stearate.
Inquiry us